TRADE NAME | CARBON % | IRON % | COBALT % | TUNGSTEN % | PARTICLE SIZE | A. D. (g/cm3) | T. D. (g/cm3) | OXYGEN | MORPHOLOGY |
---|---|---|---|---|---|---|---|---|---|
FTC | 2.5-3.5 | <0.2 | <0.6 | BAL | <45 MICRONS | 4.1-4.3 | 5.3-5.8 | <0.4% | IRREGULAR |
Fused tungsten carbide powder is a specially treated powder that is controlled and screened. It is formulated to achieve an optimum value in hardness, abrasion, erosion, and impact resistance.
Fused tungsten carbide has a particularly high degree of hardness and wear resistance. It is primarily used in advanced wear protection and tooling technology.
Fused tungsten carbide powder is used for manufacturing diamond tools such as saw blades, core bits, drill bits, and other infiltrated components. It is also used in wear applications such as welding electrodes and wires.
Properties | Tungsten | Carbon |
---|---|---|
Molecular Weight | 183.85 | 12.01 |
Appearance | Silvery | Black solid |
Melting Point | 3410 °C | 3652 - 3697 °C (sublimes) |
Boiling Point | 5900 °C | 4200 °C |
Density | 19.3 g/cm3 | 2.267 g/cm3 |
Solubility in H2O | N/A | N/A |
Electrical Resistivity | 5.65 μΩ ·m (27 °C) | N/A |
Electronegativity | 1.7 Paulings | 2.55 Paulings |
Heat of Vaporization | 806.7 kJ/mol | 128 K-Cal/gm atom at 4612 °C |
Specific Heat | 133 J/kg · °C | N/A |
Heat of Fusion | 35.3 kJ/mol | N/A |
Tensile Strength | 750 MPa | N/A |
Thermal Conductivity | 1.73 W/m ·K | 119-165 W/m/K |
Thermal Expansion | (25 °C) 4.5 µm·m-1·K-1 | (25 °C) 0.8 µm·m-1·K-1 |
Vickers Hardness | 3430 MPa | - |
Young's Modulus | 411 GPa | - |